Ngwongwo ígwè

Nkọwa nkenke:

Ngwongwo ọla bụ ọla ndị na-agbada na ihe ndị dị mma ma bụrụ ihe ndabere bụ isi maka ọtụtụ usoro obibi akwụkwọ 3D nke na-emepụta akụkụ ọla. 3D obibi, makwaara dị ka mgbakwunye n'ichepụta (AM), bụ n'ichepụta nke akụkụ na ngwaahịa na a oyi akwa-site-oyi akwa ejiji. Ma njirimara nke ntụ ntụ ọla na ụdị usoro mbipụta 3D na-ekpebi njirimara nke ngwaahịa ikpeazụ. A na-ahụ maka ntụ ntụ na-adabere n'ụzọ e si emepụta ya, nke nwere ike ibute ọdịdị dị iche iche na ịdị ọcha.

Zitere anyị email Budata dị ka PDF

Product Ihe

Ngwaahịa

Igwe anaghị agba nchara ，； 316L
Njirimara Anụ Ahụ	urughuru size	15-53 .m
	Udi	* Tụkwasị
	na-asọ asọ	40 S (Halllọ Nzukọ gafere mita)
	njupụta pụtara ìhè	3.9 g / cm
	Njupụta	7.98 g / cm3

Chemical mejupụtara	Fe	Foduru
	Kr	16 ～ 18 wt%
	Ni	10 ～ 14 wt%
	Mo	2 ～ 3 wt%
	Mn	W2 wt%
	Na	W1 wt%
	C	≤0.05 wt%
	P	≤0.045 wt%
	S	≤0.03 wt%
	O	≤0.1 wt%

Akụ Njirimara	Ikwu njupụta	Ihe ruru. 99.9%
	Ike ọdụdọ	Ihe dị ka 590 MPa
	Nwee ike	Ihe dị ka 400 MPa
	Elongation mgbe mgbaji ọkpụkpụ	Ihe dị ka. 20%
	Mgbanwe mgbanwe	Ihe dị ka 180 GPa
	Ekweghị ekwe	Nkebi 85 RR (158 HB)

Aluminom alloy ， :dị: AlSi10Mg
Njirimara Anụ Ahụ	urughuru size	15-53 .m
	Udi	* Tụkwasị
	na-asọ asọ	150 S (Halllọ Nzukọ gafere mita)
	njupụta pụtara ìhè	1,45 g / cm 3
	Njupụta	2,67 g / cm3

Chemical mejupụtara	Al	Foduru
	Na	9 ～ 10 wt%
	Mg	0.2 ～ 0.45 wt%
	Cu	≤0.05 wt%
	Mn	≤0.45 wt%
	Ni	≤0.05 wt%
	Fe	≤0.55 wt%
	Ti	≤0.15 wt%
	C	.000.0075wt%

Akụ Njirimara	Ikwu njupụta	≥95%
	Ike ọdụdọ	Ihe ruru. 330 MPa
	Nwee ike	Ihe ruru. 245 MPa
	Elongation mgbe mgbaji ọkpụkpụ	Ihe ruru. 6%
	Mgbanwe mgbanwe	Ihe ruru. 70 GPa
	Ekweghị ekwe	Ihe ruru. 120 HB

Titanium alloy ， :dị: TC4 (Ti-6Al-4V)
Njirimara Anụ Ahụ	urughuru size	15-45 .m
	Udi	* Tụkwasị
	na-asọ asọ	45 S (Halllọ Nzukọ gafere mita)
	njupụta pụtara ìhè	2,5 g / cm
	Njupụta	4.51 g / cm3

Chemical mejupụtara	Ti	Foduru
	Al	5 ～ 6.75 wt%
	V	3.5 ～ 4.5 wt%
	Fe	≤0.25 wt%
	C	≤0.02 wt%
	Y	.000.005 wt%
	O	0.14 ～ 0.16 wt%
	N	≤0.02 wt%
	Cu	≤0.1 wt%
	Ndị ọzọ	0.4 wt%

Akụ Njirimara	Ikwu njupụta	Ihe dị ka 99.9%
	Ike ọdụdọ	Ihe dị ka 1000 MPa
	Nwee ike	Ihe dị ka 900 MPa
	Elongation mgbe mgbaji ọkpụkpụ	Ihe dị ka 10%
	Mgbanwe mgbanwe	Odika 1110 GPa
	Ekweghị ekwe	Ihe dị ka 300 HV (294 HB)

Nickel-base superalloy :dị: IN718
Njirimara Anụ Ahụ	urughuru size	15-53 .m
	Udi	* Tụkwasị
	na-asọ asọ	40 S (Halllọ Nzukọ gafere mita)
	njupụta pụtara ìhè	4,1 g / cm 3
	Njupụta	8.15 g / cm3

Chemical mejupụtara	Ni	50 ～ 55 wt%
	Kr	17 ～ 22 wt%
	Nb	4.75 ～ 5.5 wt%
	Mo	2.8 ～ 3.3 wt%
	Co	W1 wt%
	C	≤0.08 wt%
	P	≤0.015 wt%
	Na	≤0.35 wt%
	Al	0.2 ～ 0.8 wt%
	Ti	0.65 ～ 1.15 wt%
	Fe	Foduru

Akụ Njirimara	Ikwu njupụta	≥99%
	Ike ọdụdọ	Ihe ruru. 980 MPa (1240 MPa mgbe a gwọchara ya)
	Nwee ike	Ihe ruru. 780 MPa (1000 MPa mgbe ọgwụgwọ ọgwụgwọ)
	Elongation mgbe mgbaji ọkpụkpụ	12 ～ 30%
	Mgbanwe mgbanwe	Ihe ruru. 160 GPa
	Ekweghị ekwe	Ihe ruru. 30 HRC (47 HRC mgbe a gwọchara ya)

Maraging Steel ， :dị: MS1
Njirimara Anụ Ahụ	urughuru size	15-53 .m
	Udi	* Tụkwasị
	na-asọ asọ	40 S (Halllọ Nzukọ gafere mita)
	njupụta pụtara ìhè	4,3 g / cm
	Njupụta	8 abA / cm

Chemical mejupụtara	Fe	Foduru
	Co	8.5 ～ 9.5 wt%
	Ni	17 ～ 19 wt%
	Mo	4.2 ～ 5.2 wt%
	Mn	≤0.1 wt%
	Ti	0.6 ～ 0.8 wt%
	C	≤0.03 wt%
	Al	0.05 ～ 0.15 wt%
	S	≤0.01 wt%
	Kr	≤0.3 wt%

Akụ Njirimara	Ikwu njupụta	≥99%
	Ike ọdụdọ	Arrpox.1090 MPa (1930 MPa mgbe ọgwụgwọ kpochara)
	Nwee ike	Arrpox.1000 MPa (1890 MPa mgbe ọgwụgwọ kpochara)
	Elongation mgbe mgbaji ọkpụkpụ	Arrpox.4%
	Mgbanwe mgbanwe	Arrpox.160 GPa (180 GPa mgbe emesịrị ọgwụgwọ)
	Ekweghị ekwe	Arrpox.35 HRC

Cobalt-chromium alloy ， :dị: MP1 (CoCr-2Lc)
Njirimara Anụ Ahụ	urughuru size	15-53 .m
	Udi	* Tụkwasị
	na-asọ asọ	40 S (Halllọ Nzukọ gafere mita)
	njupụta pụtara ìhè	4,1 g / cm 3
	Njupụta	8.3 ab / cm

Chemical mejupụtara	Co	Foduru
	Kr	26 ～ 30 wt%
	Mo	5 ～ 7 wt%
	Na	W1 wt%
	Mn	W1 wt%
	Fe	≤0.75 wt%
	C	≤0.16 wt%
	Ni	≤0.1 wt%

Akụ Njirimara	Ikwu njupụta	≥99%
	Ike ọdụdọ	Ihe dị ka 100 MPa
	Nwee ike	Ihe dị ka 900 MPa
	Elongation mgbe mgbaji ọkpụkpụ	Ihe dị ka 10%
	Mgbanwe mgbanwe	Ihe dị ka 200 GPa
	Ekweghị ekwe	35 ～ 45 HRC (323 ～ 428 HB)